Description
Lithium-ion battery separator is a kind of microporous membrane, colors ranges white to beige. It is made of polyolefin resin with wet drawing process. The product has good mechanical property and chemical stability.
It is used between positive and negative electrode of lithium ion batteries to prevent short circuit.
Specifications:
| Appearance | Ivory-White |
| Thickness | 20 ± 2 µm |
| Gas permeability | 250 – 550 Sec/100ml |
| Porosity | 38 – 44 % |
| Puncturing Strength | > 300 g |
| Tensile strength MD | > 90 Mpa |
| Tensile strength TD | > 100 Mpa |
| Film close temperature | ≤ 135 0C |
| Film break temperature | ≥ 147 0C |
| 90 0C heat shrink MD | ≤ 3.5 % |
| 90 0C heat shrink TD | ≤ 2 % |
| 105 0C heat shrink MD | ≤ 5 % |
| 105 0C heat shrink TD | ≤ 3 % |
| 120 0C heat shrink MD | ≤ 20 % |
| 120 0C heat shrink TD | ≤ 15 % |
| Appearance | Ivory-White |
| Thickness | 16 ± 2 µm |
| Gas permeability | 250 – 550 Sec/100ml |
| Porosity | 38 – 44 % |
| Puncturing Strength | > 300 g |
| Tensile strength MD | > 90 Mpa |
| Tensile strength TD | > 100 Mpa |
| Film close temperature | ≤ 135 0C |
| Film break temperature | ≥ 147 0C |
| 90 0C heat shrink MD | ≤ 3.5 % |
| 90 0C heat shrink TD | ≤ 2 % |
| 105 0C heat shrink MD | ≤ 5 % |
| 105 0C heat shrink TD | ≤ 3 % |
| 120 0C heat shrink MD | ≤ 20 % |
| 120 0C heat shrink TD | ≤ 15 % |